{"_buckets": {"deposit": "d5c57eb2-5cd9-4bad-b6be-cbc9d173ac88"}, "_deposit": {"created_by": 1, "id": "235", "owners": [1], "pid": {"revision_id": 0, "type": "depid", "value": "235"}, "status": "published"}, "_oai": {"id": "oai:ir.soken.ac.jp:00000235", "sets": ["9"]}, "author_link": ["7876", "7874", "7875"], "item_1_biblio_info_21": {"attribute_name": "書誌情報(ソート用)", "attribute_value_mlt": [{"bibliographicIssueDates": {"bibliographicIssueDate": "2004-09-30", "bibliographicIssueDateType": "Issued"}, "bibliographic_titles": [{}]}]}, "item_1_creator_2": {"attribute_name": "著者名", "attribute_type": "creator", "attribute_value_mlt": [{"creatorNames": [{"creatorName": "藤木, 聡"}], "nameIdentifiers": [{"nameIdentifier": "7874", "nameIdentifierScheme": "WEKO"}]}]}, "item_1_creator_3": {"attribute_name": "フリガナ", "attribute_type": "creator", "attribute_value_mlt": [{"creatorNames": [{"creatorName": "フジキ, サトシ"}], "nameIdentifiers": [{"nameIdentifier": "7875", "nameIdentifierScheme": "WEKO"}]}]}, "item_1_date_granted_11": {"attribute_name": "学位授与年月日", "attribute_value_mlt": [{"subitem_dategranted": "2004-09-30"}]}, "item_1_degree_grantor_5": {"attribute_name": "学位授与機関", "attribute_value_mlt": [{"subitem_degreegrantor": [{"subitem_degreegrantor_name": "総合研究大学院大学"}]}]}, "item_1_degree_name_6": {"attribute_name": "学位名", "attribute_value_mlt": [{"subitem_degreename": "博士(理学)"}]}, "item_1_description_1": {"attribute_name": "ID", "attribute_value_mlt": [{"subitem_description": "2004507", "subitem_description_type": "Other"}]}, "item_1_description_12": {"attribute_name": "要旨", "attribute_value_mlt": [{"subitem_description": " 金属内包フラーレン(M@C\u003cSUB\u003en\u003c/SUB\u003e:M=金属原子)は、金属原子をフラーレン分子に内包した分子構造をとり、金属原子からフラーレンケージに電子の移動が生じているため、金属原子の種類を変えることで、M@C\u003cSUB\u003en\u003c/SUB\u003eの電子状態を制御することができる。さらに、内包された金属原子は、フラーレンケージの中心からずれた位置に存在するので、M@C\u003cSUB\u003en\u003c/SUB\u003e分子は電気双極子モーメントを有している。また、M@C\u003cSUB\u003en\u003c/SUB\u003eは直径が~1nmの巨大な球状分子であるため、ナノメータサイズでの観察や制御が比較的容易である。このような特性から、M@C\u003cSUB\u003en\u003c/SUB\u003eは、電界効果デバイスや、双極子の配向を利用したメモリを、ナノスケールで作製するための材料としての期待が持たれている。しかしながら、M@C\u003cSUB\u003en\u003c/SUB\u003eの分子デバイスを作製するために重要な、半導体基板への吸着状態や薄膜成長に関するナノスケールの研究は、ほとんど行なわれていない。\n 走査トンネル顕微鏡(STM)は、非常に鋭く尖らせた探針を試料表面から1nm程度に保持して、試料表面を原子レベルの空間分解能で観察できる顕微鏡である。また、観察している表面の局所的な電子状態を調べることも可能であり、これは走査トンネル分光法(STS)と呼ばれる。これまでに、STM/STSを用いた金属や半導体表面に対する研究から、試料表面の構造、電子状態、気体や有機分子の試料表面への吸着、薄膜成長過程などが明らかにされている。\n このように、STMを用いることで、試料表面上でのM@C\u003cSUB\u003en\u003c/SUB\u003e分子の構造や電子状態を、ナノスケールで明らかにすることができる。本研究では、M@C\u003cSUB\u003en\u003c/SUB\u003eの中で最も効率良く精製・分離できるM@C\u003cSUB\u003e82\u003c/SUB\u003eをSi(111)-(7×7)清浄表面上に蒸着して、STMイメージから、M@C\u003cSUB\u003e82\u003c/SUB\u003eの吸着状態と膜成長過程を明らかにした。また、STSによってM@C\u003cSUB\u003e82\u003c/SUB\u003eの局所電子状態を調べ、半導体的特性を明らかにした。とくに、これまで精製・分離が困難であるため、ほとんど研究が行われていないマイナー異性体の電子状態を初めて明らかにした。\n M@C\u003cSUB\u003e82\u003c/SUB\u003eはSi(111)-(7×7)清浄表面のレストアトム上に高確率(~70%)で吸着したが、分子の配列は規則性がなくランダムであった。一方、一分子層以下の吸着においては、基板を200℃まで過熱してもSTM像に変化は見られず、M@C\u003cSUB\u003e82\u003c/SUB\u003eは表面上に固定されたままであった。また、M@C\u003cSUB\u003e82\u003c/SUB\u003e分子は第一層が完全に形成されるまでは、第二層の形成は観察されないことから、分子と基板の相互作用が強いことがわかる。さらに、第一層のM@C\u003cSUB\u003e82\u003c/SUB\u003e分子では内部構造が観察されたことから、分子の運動が室温においても凍結していることがわかった。STMにより第一層と第二層に蒸着されたM@C\u003cSUB\u003e82\u003c/SUB\u003e分子の高さを評価し、M@C\u003cSUB\u003e82\u003c/SUB\u003eの吸着様式が、第一層ではSiのdangling bondと共有結合を形成する化学吸着であり、第二層以上ではSi表面からの影響はほとんどなくなり、分子間のvan der Waals力が支配的となることを明らかにした。さらに吸着量を増やしていくと、二次元的に層形成された第一層の上に三次元的な島が形成されるStranski-Krastanov様式の結晶成長が見いだされた。\n この三次元的な島は、基板を200℃で加熱すると最密充填構造を形成することが明らかになった。最密充填構造をとる領域は、加熱時間の増加と共に広がり、最終的には100nm\u003cSUP\u003e2\u003c/SUP\u003e以上の大きさとなる。また、最密充填構造を形成するM@C\u003cSUB\u003e82\u003c/SUB\u003eは、STM観察時の電子注入によってポリマー化することがわかった。一方、500℃で加熱すると、Siと共有結合している第一層の分子を残してM@C\u003cSUB\u003e82\u003c/SUB\u003eは昇華することを見いだされた。これらは、第二層以上では、分子の吸着過程を基板温度により制御することによって、M@C\u003cSUB\u003e82\u003c/SUB\u003eの積層状態をコントロールできる可能性を示唆している。\n STS測定をM@C\u003cSUB\u003e82\u003c/SUB\u003eのメジャー異性体だけでなく、マイナー異性体に対しても行なった。メジャー異性体およびマイナー異性体の最高被占有軌道(HOMO)-最低空軌道(LUMO)ギャップは、それぞれ~0.7および~1.0eVであり、両者とも微少ギャップ半導体であることを明らかにした。メジャー異性体のHOMO-LUMOgapが、マイナー異性体の値よりも小さい値を示しており、これは、薄膜の電気抵抗率測定から評価したエネルギーギャップEgでも同様の傾向[1]が見られている。さらに、STSから評価したHOMO-LUMOgapの大きさは、紫外線光電子分光(UPS)から求めたEg[2]の2倍程度の値である。この原因として、光電子分光法では、HOMOからフェルミ準位までのエネルギー差をEgとして評価している可能性がある\n\n[1] Y. Rikiishi, Y. Kubozono, T. Hosokawa, K. Shibata, Y.Haruyama, Y. Takabayashi, A. Fujiwara, S. Kobayashi, S. Mori, and Y. Iwasa, J. Phys. Chem. 108, 7580 (2004).\n\n[2] S. Hino, H. Takahashi, K. Iwasaki, K. Matsumoto, T. Miyazaki, S. Hasagawa, K. Kikuchi, and Y. Achiba, Phys. Rev. Lett. 71, 4261 (1993).", "subitem_description_type": "Other"}]}, "item_1_description_18": {"attribute_name": "フォーマット", "attribute_value_mlt": [{"subitem_description": "application/pdf", "subitem_description_type": "Other"}]}, "item_1_description_7": {"attribute_name": "学位記番号", "attribute_value_mlt": [{"subitem_description": "総研大甲第798号", "subitem_description_type": "Other"}]}, "item_1_select_14": {"attribute_name": "所蔵", "attribute_value_mlt": [{"subitem_select_item": "有"}]}, "item_1_select_16": {"attribute_name": "複写", "attribute_value_mlt": [{"subitem_select_item": "印刷物から複写可"}]}, "item_1_select_17": {"attribute_name": "公開状況", "attribute_value_mlt": [{"subitem_select_item": "要旨のみ公開"}]}, "item_1_select_8": {"attribute_name": "研究科", "attribute_value_mlt": [{"subitem_select_item": "物理科学研究科"}]}, "item_1_select_9": {"attribute_name": "専攻", "attribute_value_mlt": [{"subitem_select_item": "07 構造分子科学専攻"}]}, "item_1_text_10": {"attribute_name": "学位授与年度", "attribute_value_mlt": [{"subitem_text_value": "2004"}]}, "item_1_text_20": {"attribute_name": "業務メモ", "attribute_value_mlt": [{"subitem_text_value": "(2017年11月15日)本籍など個人情報の記載がある旧要旨・審査要旨を個人情報のない新しいものに差し替えた。承諾書を確認した。"}]}, "item_creator": {"attribute_name": "著者", "attribute_type": "creator", "attribute_value_mlt": [{"creatorNames": [{"creatorName": "FUJIKI, Satoshi", "creatorNameLang": "en"}], "nameIdentifiers": [{"nameIdentifier": "7876", "nameIdentifierScheme": "WEKO"}]}]}, "item_files": {"attribute_name": "ファイル情報", "attribute_type": "file", "attribute_value_mlt": [{"accessrole": "open_date", "date": [{"dateType": "Available", "dateValue": "2016-02-17"}], "displaytype": "simple", "download_preview_message": "", "file_order": 0, "filename": "甲798_要旨.pdf", "filesize": [{"value": "319.9 kB"}], "format": "application/pdf", "future_date_message": "", "is_thumbnail": false, "licensetype": "license_11", "mimetype": "application/pdf", "size": 319900.0, "url": {"label": "要旨・審査要旨 / Abstract, Screening Result", "url": "https://ir.soken.ac.jp/record/235/files/甲798_要旨.pdf"}, "version_id": "89fdb6a3-9361-493a-a766-c02ede0597c3"}]}, "item_language": {"attribute_name": "言語", "attribute_value_mlt": [{"subitem_language": "eng"}]}, "item_resource_type": {"attribute_name": "資源タイプ", "attribute_value_mlt": [{"resourcetype": "thesis", "resourceuri": "http://purl.org/coar/resource_type/c_46ec"}]}, "item_title": "Scanning Tunneling Microscopy and Spectroscopy Studies of Endohedral Metallofullerenes on Well-defined Si Surface", "item_titles": {"attribute_name": "タイトル", "attribute_value_mlt": [{"subitem_title": "Scanning Tunneling Microscopy and Spectroscopy Studies of Endohedral Metallofullerenes on Well-defined Si Surface"}, {"subitem_title": "Scanning Tunneling Microscopy and Spectroscopy Studies of Endohedral Metallofullerenes on Well-defined Si Surface", "subitem_title_language": "en"}]}, "item_type_id": "1", "owner": "1", "path": ["9"], "permalink_uri": "https://ir.soken.ac.jp/records/235", "pubdate": {"attribute_name": "公開日", "attribute_value": "2010-02-22"}, "publish_date": "2010-02-22", "publish_status": "0", "recid": "235", "relation": {}, "relation_version_is_last": true, "title": ["Scanning Tunneling Microscopy and Spectroscopy Studies of Endohedral Metallofullerenes on Well-defined Si Surface"], "weko_shared_id": 1}
Scanning Tunneling Microscopy and Spectroscopy Studies of Endohedral Metallofullerenes on Well-defined Si Surface
https://ir.soken.ac.jp/records/235
https://ir.soken.ac.jp/records/235a104fbb3-3eff-4ae3-a83b-fb0b76c42e25
名前 / ファイル | ライセンス | アクション |
---|---|---|
要旨・審査要旨 / Abstract, Screening Result (319.9 kB)
|
Item type | 学位論文 / Thesis or Dissertation(1) | |||||
---|---|---|---|---|---|---|
公開日 | 2010-02-22 | |||||
タイトル | ||||||
タイトル | Scanning Tunneling Microscopy and Spectroscopy Studies of Endohedral Metallofullerenes on Well-defined Si Surface | |||||
タイトル | ||||||
言語 | en | |||||
タイトル | Scanning Tunneling Microscopy and Spectroscopy Studies of Endohedral Metallofullerenes on Well-defined Si Surface | |||||
言語 | ||||||
言語 | eng | |||||
資源タイプ | ||||||
資源タイプ識別子 | http://purl.org/coar/resource_type/c_46ec | |||||
資源タイプ | thesis | |||||
著者名 |
藤木, 聡
× 藤木, 聡 |
|||||
フリガナ |
フジキ, サトシ
× フジキ, サトシ |
|||||
著者 |
FUJIKI, Satoshi
× FUJIKI, Satoshi |
|||||
学位授与機関 | ||||||
学位授与機関名 | 総合研究大学院大学 | |||||
学位名 | ||||||
学位名 | 博士(理学) | |||||
学位記番号 | ||||||
内容記述タイプ | Other | |||||
内容記述 | 総研大甲第798号 | |||||
研究科 | ||||||
値 | 物理科学研究科 | |||||
専攻 | ||||||
値 | 07 構造分子科学専攻 | |||||
学位授与年月日 | ||||||
学位授与年月日 | 2004-09-30 | |||||
学位授与年度 | ||||||
2004 | ||||||
要旨 | ||||||
内容記述タイプ | Other | |||||
内容記述 | 金属内包フラーレン(M@C<SUB>n</SUB>:M=金属原子)は、金属原子をフラーレン分子に内包した分子構造をとり、金属原子からフラーレンケージに電子の移動が生じているため、金属原子の種類を変えることで、M@C<SUB>n</SUB>の電子状態を制御することができる。さらに、内包された金属原子は、フラーレンケージの中心からずれた位置に存在するので、M@C<SUB>n</SUB>分子は電気双極子モーメントを有している。また、M@C<SUB>n</SUB>は直径が~1nmの巨大な球状分子であるため、ナノメータサイズでの観察や制御が比較的容易である。このような特性から、M@C<SUB>n</SUB>は、電界効果デバイスや、双極子の配向を利用したメモリを、ナノスケールで作製するための材料としての期待が持たれている。しかしながら、M@C<SUB>n</SUB>の分子デバイスを作製するために重要な、半導体基板への吸着状態や薄膜成長に関するナノスケールの研究は、ほとんど行なわれていない。 走査トンネル顕微鏡(STM)は、非常に鋭く尖らせた探針を試料表面から1nm程度に保持して、試料表面を原子レベルの空間分解能で観察できる顕微鏡である。また、観察している表面の局所的な電子状態を調べることも可能であり、これは走査トンネル分光法(STS)と呼ばれる。これまでに、STM/STSを用いた金属や半導体表面に対する研究から、試料表面の構造、電子状態、気体や有機分子の試料表面への吸着、薄膜成長過程などが明らかにされている。 このように、STMを用いることで、試料表面上でのM@C<SUB>n</SUB>分子の構造や電子状態を、ナノスケールで明らかにすることができる。本研究では、M@C<SUB>n</SUB>の中で最も効率良く精製・分離できるM@C<SUB>82</SUB>をSi(111)-(7×7)清浄表面上に蒸着して、STMイメージから、M@C<SUB>82</SUB>の吸着状態と膜成長過程を明らかにした。また、STSによってM@C<SUB>82</SUB>の局所電子状態を調べ、半導体的特性を明らかにした。とくに、これまで精製・分離が困難であるため、ほとんど研究が行われていないマイナー異性体の電子状態を初めて明らかにした。 M@C<SUB>82</SUB>はSi(111)-(7×7)清浄表面のレストアトム上に高確率(~70%)で吸着したが、分子の配列は規則性がなくランダムであった。一方、一分子層以下の吸着においては、基板を200℃まで過熱してもSTM像に変化は見られず、M@C<SUB>82</SUB>は表面上に固定されたままであった。また、M@C<SUB>82</SUB>分子は第一層が完全に形成されるまでは、第二層の形成は観察されないことから、分子と基板の相互作用が強いことがわかる。さらに、第一層のM@C<SUB>82</SUB>分子では内部構造が観察されたことから、分子の運動が室温においても凍結していることがわかった。STMにより第一層と第二層に蒸着されたM@C<SUB>82</SUB>分子の高さを評価し、M@C<SUB>82</SUB>の吸着様式が、第一層ではSiのdangling bondと共有結合を形成する化学吸着であり、第二層以上ではSi表面からの影響はほとんどなくなり、分子間のvan der Waals力が支配的となることを明らかにした。さらに吸着量を増やしていくと、二次元的に層形成された第一層の上に三次元的な島が形成されるStranski-Krastanov様式の結晶成長が見いだされた。 この三次元的な島は、基板を200℃で加熱すると最密充填構造を形成することが明らかになった。最密充填構造をとる領域は、加熱時間の増加と共に広がり、最終的には100nm<SUP>2</SUP>以上の大きさとなる。また、最密充填構造を形成するM@C<SUB>82</SUB>は、STM観察時の電子注入によってポリマー化することがわかった。一方、500℃で加熱すると、Siと共有結合している第一層の分子を残してM@C<SUB>82</SUB>は昇華することを見いだされた。これらは、第二層以上では、分子の吸着過程を基板温度により制御することによって、M@C<SUB>82</SUB>の積層状態をコントロールできる可能性を示唆している。 STS測定をM@C<SUB>82</SUB>のメジャー異性体だけでなく、マイナー異性体に対しても行なった。メジャー異性体およびマイナー異性体の最高被占有軌道(HOMO)-最低空軌道(LUMO)ギャップは、それぞれ~0.7および~1.0eVであり、両者とも微少ギャップ半導体であることを明らかにした。メジャー異性体のHOMO-LUMOgapが、マイナー異性体の値よりも小さい値を示しており、これは、薄膜の電気抵抗率測定から評価したエネルギーギャップEgでも同様の傾向[1]が見られている。さらに、STSから評価したHOMO-LUMOgapの大きさは、紫外線光電子分光(UPS)から求めたEg[2]の2倍程度の値である。この原因として、光電子分光法では、HOMOからフェルミ準位までのエネルギー差をEgとして評価している可能性がある [1] Y. Rikiishi, Y. Kubozono, T. Hosokawa, K. Shibata, Y.Haruyama, Y. Takabayashi, A. Fujiwara, S. Kobayashi, S. Mori, and Y. Iwasa, J. Phys. Chem. 108, 7580 (2004). [2] S. Hino, H. Takahashi, K. Iwasaki, K. Matsumoto, T. Miyazaki, S. Hasagawa, K. Kikuchi, and Y. Achiba, Phys. Rev. Lett. 71, 4261 (1993). |
|||||
所蔵 | ||||||
値 | 有 | |||||
フォーマット | ||||||
内容記述タイプ | Other | |||||
内容記述 | application/pdf |